Chlorinated Polyethylene | Elaslen

202KB
252B
301AS
301MA
302NAC
303A
303BS
351AYS
352NA
352GB
353AY
401AY
402B
402NA
404B

202KB

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	22.0∼25.0	wt%	SDK Method
Specific Gravity	1.05∼1.09	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	9,0	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	23	J/g	DSC
Tensile Strenght	11,0	MPa	JIS K6251
Elongation	700	%	JIS K6251
100% Modulus	3,8	MPa	JIS K6251
Hardness	82	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-27	ºC	JIS K6261
Volume Resistivity	4 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	5 x 10^-3	-	ASTM D150
Dielectric Content	3,6	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

252B

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	22.0∼25.0	wt%	SDK Method
Specific Gravity	1.05∼1.09	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	3,0	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	20	J/g	DSC
Tensile Strenght	14,0	MPa	JIS K6251
Elongation	850	%	JIS K6251
100% Modulus	3,1	MPa	JIS K6251
Hardness	82	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-27	ºC	JIS K6261
Volume Resistivity	4 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	5 x 10^-3	-	ASTM D150
Dielectric Content	3,6	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

301AS

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	29.0∼33.0	wt%	SDK Method
Specific Gravity	1.10∼1.14	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	1,7	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	85	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	11,1	MPa	JIS K6251
Elongation	950	%	JIS K6251
100% Modulus	1,0	MPa	JIS K6251
Hardness	58	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-32	ºC	JIS K6261
Volume Resistivity	3 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	1 x 10^-2	-	ASTM D150
Dielectric Content	4,3	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

301MA

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	30.0∼33.0	wt%	SDK Method
Specific Gravity	1.10∼1.14	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	0,1	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	11,8	MPa	JIS K6251
Elongation	900	%	JIS K6251
100% Modulus	1,0	MPa	JIS K6251
Hardness	60	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-32	ºC	JIS K6261
Volume Resistivity	2 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	1 x 10^-2	-	ASTM D150
Dielectric Content	4,3	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

302NAC

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	26.5∼29.5	wt%	SDK Method
Specific Gravity	1.08∼1.13	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	12	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	45	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	9,8	MPa	JIS K6251
Elongation	1100	%	JIS K6251
100% Modulus	1,1	MPa	JIS K6251
Hardness	58	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-33	ºC	JIS K6261
Volume Resistivity	3 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	1 x 10^-2	-	ASTM D150
Dielectric Content	4,3	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

303A

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	30.0∼33.0	wt%	SDK Method
Specific Gravity	1.10∼1.14	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	120	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	20	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	6,9	MPa	JIS K6251
Elongation	800	%	JIS K6251
100% Modulus	1,5	MPa	JIS K6251
Hardness	60	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-24	ºC	JIS K6261
Volume Resistivity	3 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	1 x 10^-2	-	ASTM D150
Dielectric Content	4,3	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

303BS

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	30.0∼33.0	wt%	SDK Method
Specific Gravity	1.12∼1.15	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	25	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	50	J/g	DSC
Tensile Strenght	11,1	MPa	JIS K6251
Elongation	800	%	JIS K6251
100% Modulus	2,9	MPa	JIS K6251
Hardness	78	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-16	ºC	JIS K6261
Volume Resistivity	4 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	7 x 10^-3	-	ASTM D150
Dielectric Content	3,7	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

351AYS

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	32.0∼37.0	wt%	SDK Method
Specific Gravity	1.12∼1.19	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	1,8	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	90	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	10,5	MPa	JIS K6251
Elongation	1000	%	JIS K6251
100% Modulus	0,9	MPa	JIS K6251
Hardness	56	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-24	ºC	JIS K6261
Volume Resistivity	2 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	2 x 10^-2	-	ASTM D150
Dielectric Content	4,5	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

352NA

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	33.5∼36.5	wt%	SDK Method
Specific Gravity	1.13∼1.17	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	9,0	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	55	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	7,8	MPa	JIS K6251
Elongation	950	%	JIS K6251
100% Modulus	0,8	MPa	JIS K6251
Hardness	54	JIS A	JIS K6253
Brittle Temperature	-65	ºC	JIS K6261
Freezing Point	-28	ºC	JIS K6261
Volume Resistivity	2 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	2 x 10^-2	-	ASTM D150
Dielectric Content	4,5	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

352GB

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	34.0∼37.0	wt%	SDK Method
Specific Gravity	1.16∼1.20	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	0,8	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	20	J/g	DSC
Tensile Strenght	12,7	MPa	JIS K6251
Elongation	400	%	JIS K6251
100% Modulus	2,5	MPa	JIS K6251
Hardness	76	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-17	ºC	JIS K6261
Volume Resistivity	3 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	9 x 10^-3	-	ASTM D150
Dielectric Content	4,0	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

353AY

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	33.0∼36.0	wt%	SDK Method
Specific Gravity	1.14∼1.18	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	65	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	20	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	5,2	MPa	JIS K6251
Elongation	1200	%	JIS K6251
100% Modulus	0,8	MPa	JIS K6251
Hardness	50	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-28	ºC	JIS K6261
Volume Resistivity	2 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	2 x 10^-2	-	ASTM D150
Dielectric Content	4,5	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

401AY

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	37.5∼41.5	wt%	SDK Method
Specific Gravity	1.18∼1.22	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	1,6	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	105	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	9,9	MPa	JIS K6251
Elongation	800	%	JIS K6251
100% Modulus	0,9	MPa	JIS K6251
Hardness	58	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-15	ºC	JIS K6261
Volume Resistivity	1 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	4 x 10^-2	-	ASTM D150
Dielectric Content	4,7	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

402B

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	37.5∼41.5	wt%	SDK Method
Specific Gravity	1.19∼1.23	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	1,2	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	10	J/g	DSC
Tensile Strenght	15,0	MPa	JIS K6251
Elongation	500	%	JIS K6251
100% Modulus	2,5	MPa	JIS K6251
Hardness	65	JIS A	JIS K6253
Brittle Temperature	-55	ºC	JIS K6261
Freezing Point	-8	ºC	JIS K6261
Volume Resistivity	1 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	1 x 10^-2	-	ASTM D150
Dielectric Content	4,4	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

402NA

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	37.5∼40.5	wt%	SDK Method
Specific Gravity	1.18∼1.22	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	8,0	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	65	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	6,9	MPa	JIS K6251
Elongation	700	%	JIS K6251
100% Modulus	0,9	MPa	JIS K6251
Hardness	58	JIS A	JIS K6253
Brittle Temperature	-55	ºC	JIS K6261
Freezing Point	-15	ºC	JIS K6261
Volume Resistivity	1 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	4 x 10^-2	-	ASTM D150
Dielectric Content	4,7	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

404B

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	38.0∼41.0	wt%	SDK Method
Specific Gravity	1.19∼1.23	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	25	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	29	J/g	DSC
Tensile Strenght	16,7	MPa	JIS K6251
Elongation	550	%	JIS K6251
100% Modulus	2,5	MPa	JIS K6251
Hardness	80	JIS A	JIS K6253
Brittle Temperature	-55	ºC	JIS K6261
Freezing Point	-1	ºC	JIS K6261
Volume Resistivity	2 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	9 x 10^-3	-	ASTM D150
Dielectric Content	4,0	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.