FR ABS Modifier

Choose from our recommended Grades below

202KB
(Chlorinated Polyethylene Elaslen®)
252B
(Chlorinated Polyethylene Elaslen®)
303A
(Chlorinated Polyethylene Elaslen®)
303BS
(Chlorinated Polyethylene Elaslen®)
353AY
(Chlorinated Polyethylene Elaslen®)

202KB

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	22.0∼25.0	wt%	SDK Method
Specific Gravity	1.05∼1.09	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	9,0	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	23	J/g	DSC
Tensile Strenght	11,0	MPa	JIS K6251
Elongation	700	%	JIS K6251
100% Modulus	3,8	MPa	JIS K6251
Hardness	82	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-27	ºC	JIS K6261
Volume Resistivity	4 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	5 x 10^-3	-	ASTM D150
Dielectric Content	3,6	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

252B

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	22.0∼25.0	wt%	SDK Method
Specific Gravity	1.05∼1.09	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	3,0	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	20	J/g	DSC
Tensile Strenght	14,0	MPa	JIS K6251
Elongation	850	%	JIS K6251
100% Modulus	3,1	MPa	JIS K6251
Hardness	82	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-27	ºC	JIS K6261
Volume Resistivity	4 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	5 x 10^-3	-	ASTM D150
Dielectric Content	3,6	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

303A

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	30.0∼33.0	wt%	SDK Method
Specific Gravity	1.10∼1.14	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	120	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	20	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	6,9	MPa	JIS K6251
Elongation	800	%	JIS K6251
100% Modulus	1,5	MPa	JIS K6251
Hardness	60	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-24	ºC	JIS K6261
Volume Resistivity	3 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	1 x 10^-2	-	ASTM D150
Dielectric Content	4,3	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

303BS

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	30.0∼33.0	wt%	SDK Method
Specific Gravity	1.12∼1.15	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	25	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	50	J/g	DSC
Tensile Strenght	11,1	MPa	JIS K6251
Elongation	800	%	JIS K6251
100% Modulus	2,9	MPa	JIS K6251
Hardness	78	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-16	ºC	JIS K6261
Volume Resistivity	4 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	7 x 10^-3	-	ASTM D150
Dielectric Content	3,7	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

353AY

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	33.0∼36.0	wt%	SDK Method
Specific Gravity	1.14∼1.18	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	65	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	20	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	5,2	MPa	JIS K6251
Elongation	1200	%	JIS K6251
100% Modulus	0,8	MPa	JIS K6251
Hardness	50	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-28	ºC	JIS K6261
Volume Resistivity	2 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	2 x 10^-2	-	ASTM D150
Dielectric Content	4,5	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.