Flexible PVC Modifier

Choose from our recommended Grades below

202KB
(Chlorinated Polyethylene Elaslen®)
252B
(Chlorinated Polyethylene Elaslen®)
351AYS
(Chlorinated Polyethylene Elaslen®)
352GB
(Chlorinated Polyethylene Elaslen®)
401AY
(Chlorinated Polyethylene Elaslen®)
402B
(Chlorinated Polyethylene Elaslen®)
402NA
(Chlorinated Polyethylene Elaslen®)

202KB

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	22.0∼25.0	wt%	SDK Method
Specific Gravity	1.05∼1.09	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	9,0	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	23	J/g	DSC
Tensile Strenght	11,0	MPa	JIS K6251
Elongation	700	%	JIS K6251
100% Modulus	3,8	MPa	JIS K6251
Hardness	82	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-27	ºC	JIS K6261
Volume Resistivity	4 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	5 x 10^-3	-	ASTM D150
Dielectric Content	3,6	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

252B

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	22.0∼25.0	wt%	SDK Method
Specific Gravity	1.05∼1.09	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	3,0	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	20	J/g	DSC
Tensile Strenght	14,0	MPa	JIS K6251
Elongation	850	%	JIS K6251
100% Modulus	3,1	MPa	JIS K6251
Hardness	82	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-27	ºC	JIS K6261
Volume Resistivity	4 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	5 x 10^-3	-	ASTM D150
Dielectric Content	3,6	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

351AYS

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	32.0∼37.0	wt%	SDK Method
Specific Gravity	1.12∼1.19	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	1,8	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	90	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	10,5	MPa	JIS K6251
Elongation	1000	%	JIS K6251
100% Modulus	0,9	MPa	JIS K6251
Hardness	56	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-24	ºC	JIS K6261
Volume Resistivity	2 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	2 x 10^-2	-	ASTM D150
Dielectric Content	4,5	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

352GB

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	34.0∼37.0	wt%	SDK Method
Specific Gravity	1.16∼1.20	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	0,8	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	20	J/g	DSC
Tensile Strenght	12,7	MPa	JIS K6251
Elongation	400	%	JIS K6251
100% Modulus	2,5	MPa	JIS K6251
Hardness	76	JIS A	JIS K6253
Brittle Temperature	-60	ºC	JIS K6261
Freezing Point	-17	ºC	JIS K6261
Volume Resistivity	3 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	9 x 10^-3	-	ASTM D150
Dielectric Content	4,0	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

401AY

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	37.5∼41.5	wt%	SDK Method
Specific Gravity	1.18∼1.22	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	1,6	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	105	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	9,9	MPa	JIS K6251
Elongation	800	%	JIS K6251
100% Modulus	0,9	MPa	JIS K6251
Hardness	58	JIS A	JIS K6253
Brittle Temperature	<-70	ºC	JIS K6261
Freezing Point	-15	ºC	JIS K6261
Volume Resistivity	1 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	4 x 10^-2	-	ASTM D150
Dielectric Content	4,7	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

402B

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	37.5∼41.5	wt%	SDK Method
Specific Gravity	1.19∼1.23	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	1,2	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	-	-	JIS K6300 (121ºC) ML1+4
Crystallinity	10	J/g	DSC
Tensile Strenght	15,0	MPa	JIS K6251
Elongation	500	%	JIS K6251
100% Modulus	2,5	MPa	JIS K6251
Hardness	65	JIS A	JIS K6253
Brittle Temperature	-55	ºC	JIS K6261
Freezing Point	-8	ºC	JIS K6261
Volume Resistivity	1 x 10¹⁶	Ω-cm	ASTM D257
Dielectric Tangent	1 x 10^-2	-	ASTM D150
Dielectric Content	4,4	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.

402NA

DATA SHEET

PROPERTY	VALUE	UNIT	TEST METHOD
Chlorine Content	37.5∼40.5	wt%	SDK Method
Specific Gravity	1.18∼1.22	-	JIS K7112
Water	≤1.0	wt%	SDK method
Melt Flow Rate	8,0	g/10min	JIS K7210 180ºC 21.6kg
Mooney Viscosity	65	-	JIS K6300 (121ºC) ML1+4
Crystallinity	<2	J/g	DSC
Tensile Strenght	6,9	MPa	JIS K6251
Elongation	700	%	JIS K6251
100% Modulus	0,9	MPa	JIS K6251
Hardness	58	JIS A	JIS K6253
Brittle Temperature	-55	ºC	JIS K6261
Freezing Point	-15	ºC	JIS K6261
Volume Resistivity	1 x 10¹⁵	Ω-cm	ASTM D257
Dielectric Tangent	4 x 10^-2	-	ASTM D150
Dielectric Content	4,7	%	ASTM D150
The above is typical data and it is not guaranteed by either Showa Denko or SEL.